Dental Zirconia Disc Supplier 98mm High Translucent CAD CAM Zirconia Blank Factory China
Key Attributes
Nombre de la marca:
Kyozir
Número de modelo:
ST-ML
Lugar de origen:
Porcelana
Certificación:
ISO , CE , FDA
Cantidad mínima de pedido:
1
Precio:
20-60 USD
Capacidad de suministro:
2000 unidades/día
Tiempo de entrega:
7-10 días laborables
Standard Packaging:
1 caja/unidades
Especificaciones
Características destacadas
98mm high translucent zirconia disc
,CAD CAM zirconia blank
,dental zirconia disc supplier
Nombre:
Bloque de zirconio multicapa
Fortaleza:
>800 MPa
Translucidez:
42%-46%
Altura:
10-25 mm
Sombras:
A1-D4/BL1-BL4
temperatura de la sinterización:
1530°C
Descripción de producto
ST-ML High Translucent CAD/CAM Zirconia Disc
Kyozir ST-ML Dental Zirconia Blank is a high-performance dental material featuring exceptional aesthetics and strength. With 46% transparency and flexural strength exceeding 800 MPa, this multilayer zirconia block utilizes transition layer technology to replicate the natural appearance of teeth while reducing chroma towards the cut area.
Key Specifications
- High Translucency (45%-46%): Natural enamel-like aesthetics for anterior restorations
- High Strength (≥800 MPa): Reliable for crowns and 3-unit bridges
- Universal CAD/CAM Compatibility: Fits most milling systems on the market
Product Advantages
Natural Esthetics
45-46% translucency for lifelike tooth appearance
Strong & Durable
Flexural strength ≥800 MPa ensures long-term stability
Precise Fit
Excellent milling accuracy and edge stability
Stable Material Performance
Low shrinkage and consistent sintering results
Compatible with All Major CAD/CAM Systems
Universal compatibility for seamless integration
Case Examples
Physical Characteristics
| Property | Value |
|---|---|
| Density before sintering | 3.15±0.05 g/cm³ |
| Density after sintering | 6.07±0.02 g/cm³ |
| CTE (25-500℃) | (10.4±0.5)×10⁻⁶ K⁻¹ |
| Accelerated aging surface monoclinic phase content | <15% |
| Chemical solubility after sintering | <100 μg/cm |
| Radioactivity | <0.1 Bq/g |
| Sintering temperature | 1530℃ |
Dental Zirconia Shade Guide Color Chart
Clinical Applications
Full Contour Anterior Crown
Posterior Bridge (3 units)
Full Contour Bridge (4 units)
Full Contour Bridge (>4 units)
Anterior Coping
Reduced Posterior Bridge (3 units)
Posterior Coping
Anterior Coping Bridge (3 units)
Why Choose Kyozir?
Direct Factory Supply - Kyozir
- 15+ years of dental zirconia manufacturing experience
- Advanced CAD/CAM material R&D system
- Strict ISO / CE / FDA certified production
- Stable raw material supply
- Exported to 60+ countries worldwide
Quality Assurance System
- Raw material inspection before production
- Density & purity testing
- Flexural strength testing
- Translucency consistency check
- Sintering shrinkage verification
- Final batch QC before shipment