Dental Zirconia Disc Supplier 98mm High Translucent CAD CAM Zirconia Blank Factory China
Key Attributes
Marchio:
Kyozir
Numero di modello:
ST-ML
Luogo di origine:
Cina
Certificazione:
ISO , CE , FDA
Quantità di ordine minimo:
1
Prezzo:
20-60 USD
Capacità di approvvigionamento:
2000 pezzi/giorno
Tempo di consegna:
7-10 giorni lavorativi
Standard Packaging:
1 scatola/pz
Specifiche
Funzionalità principali
98mm high translucent zirconia disc
,CAD CAM zirconia blank
,dental zirconia disc supplier
Nome:
Blocco di zirconio multistrato
Forza:
>800 MPa
Traslucenza:
42%-46%
Altezza:
10-25 mm
Tonalità:
A1-D4 / BL1-BL4
temperatura di sinterizzazione:
1530°C
Descrizione di prodotto
ST-ML High Translucent CAD/CAM Zirconia Disc
Kyozir ST-ML Dental Zirconia Blank is a high-performance dental material featuring exceptional aesthetics and strength. With 46% transparency and flexural strength exceeding 800 MPa, this multilayer zirconia block utilizes transition layer technology to replicate the natural appearance of teeth while reducing chroma towards the cut area.
Key Specifications
- High Translucency (45%-46%): Natural enamel-like aesthetics for anterior restorations
- High Strength (≥800 MPa): Reliable for crowns and 3-unit bridges
- Universal CAD/CAM Compatibility: Fits most milling systems on the market
Product Advantages
Natural Esthetics
45-46% translucency for lifelike tooth appearance
Strong & Durable
Flexural strength ≥800 MPa ensures long-term stability
Precise Fit
Excellent milling accuracy and edge stability
Stable Material Performance
Low shrinkage and consistent sintering results
Compatible with All Major CAD/CAM Systems
Universal compatibility for seamless integration
Case Examples
Physical Characteristics
| Property | Value |
|---|---|
| Density before sintering | 3.15±0.05 g/cm³ |
| Density after sintering | 6.07±0.02 g/cm³ |
| CTE (25-500℃) | (10.4±0.5)×10⁻⁶ K⁻¹ |
| Accelerated aging surface monoclinic phase content | <15% |
| Chemical solubility after sintering | <100 μg/cm |
| Radioactivity | <0.1 Bq/g |
| Sintering temperature | 1530℃ |
Dental Zirconia Shade Guide Color Chart
Clinical Applications
Full Contour Anterior Crown
Posterior Bridge (3 units)
Full Contour Bridge (4 units)
Full Contour Bridge (>4 units)
Anterior Coping
Reduced Posterior Bridge (3 units)
Posterior Coping
Anterior Coping Bridge (3 units)
Why Choose Kyozir?
Direct Factory Supply - Kyozir
- 15+ years of dental zirconia manufacturing experience
- Advanced CAD/CAM material R&D system
- Strict ISO / CE / FDA certified production
- Stable raw material supply
- Exported to 60+ countries worldwide
Quality Assurance System
- Raw material inspection before production
- Density & purity testing
- Flexural strength testing
- Translucency consistency check
- Sintering shrinkage verification
- Final batch QC before shipment