Kyozir ST-ML Super Translucent Zirconia Cost-Effective Dental Zirconia for Lab
Key Attributes
ブランド名:
Kyozir
モデル番号:
ST-ML
原産地:
中国
認証:
ISO , CE , FDA
最小注文数量:
1
価格:
20-60 USD
供給能力:
2000個/日
配達時間:
7～10営業日
Standard Packaging:
1箱/個
指定
注目すべき 特徴
Super Translucent Zirconia Dental Blocks
,Cost-Effective Dental Zirconia for Lab
,ST-ML Translucent Zirconia with Warranty
名前:
多層ジルコニアブロック
強さ:
＞800MPa
半透明性:
42%-46%
身長:
10-25mm
陰:
A1～D4 / BL1～BL4
焼結の温度:
1530°C
製品の説明
Kyozir ST-ML Super Translucent Zirconia Cost-Effective Dental Zirconia for Lab
High Esthetics
42%-46% Translucency
High Strength
>800MPa
High Value
Maximize Lab Profit
Designed for modern dental labs, Kyozir ST-ML combines exceptional translucency (42%-46%) with high strength (>800MPa) to deliver natural, beautiful restorations—at a cost that makes your lab more competitive.
Lower Cost. Higher Value.
Kyozir ST-ML helps labs reduce material cost by up to 30% compared with similar products, without sacrificing quality.
Why Dental Labs Choose ST-ML Zirconia?
Cost Control Without Quality Loss
ST-ML is designed to reduce material cost while maintaining high aesthetic performance.
Higher Case Profitability
Fewer remakes + stable color consistency = higher efficiency per case.
Natural Esthetic Outcome
Super translucent structure improves light diffusion for anterior restorations.
Stable Batch-to-Batch Quality
Industrial-scale production ensures consistent results for dental labs.
Technical Specifications
| Property | Value |
|---|---|
| Density before sintering | 3.15±0.05 g/cm³ |
| Density after sintering | 6.07±0.02 g/cm³ |
| CTE (25-500℃) | (10.4±0.5)×10⁻⁶ K⁻¹ |
| Accelerated aging surface monoclinic phase content | <15% |
| Chemical solubility after sintering | <100 μg/cm |
| Radioactivity | <0.1 Bq/g |
| Sintering temperature | 1530℃ |
Clinical Applications
Full Contour Anterior Crown
Posterior Bridge (3 units)
Full Contour Bridge (4 units)
Full Contour Bridge (>4 units)
Anterior Coping
Reduced Posterior Bridge (3 units)
Posterior Coping
Anterior Coping Bridge (3 units)