China Zircon Multilayer Zirconia Block for CAD CAM Dental Restorations
Key Attributes
Tên thương hiệu:
Kyozir
Số mẫu:
ST-ML
Nơi xuất xứ:
Trung Quốc
Chứng nhận:
ISO , CE , FDA
Số lượng đơn hàng tối thiểu:
1
Giá bán:
20-60 USD
Khả năng cung cấp:
2000 chiếc / ngày
Thời gian giao hàng:
7-10 ngày làm việc
Standard Packaging:
1 hộp/chiếc
Thông số kỹ thuật
Tính năng nổi bật
Zirconia block for CAD CAM
,Multilayer zirconia dental block
,Dental zirconia restoration block
Tên:
Khối Zirconia nhiều lớp
Sức mạnh:
＞800 Mpa
độ trong suốt:
42%-46%
Chiều cao:
10-25mm
sắc thái:
A1-D4/BL1-BL4
nhiệt độ thiêu kết:
1530oC
Mô tả sản phẩm
Kyozir ST-ML Multilayer Zirconia Block for CAD/CAM Dental Restorations
Kyozir ST-ML Dental Zirconia Blank is a high-performance dental material featuring exceptional aesthetics and strength. With 46% transparency and flexural strength exceeding 800 MPa, this multilayer zirconia block utilizes transition layer technology to replicate the natural appearance of teeth while reducing chroma towards the cut area.
Key Specifications
- High Translucency (45% - 46%)
- High Strength (≥800 MPa)
- Universal CAD/CAM Compatibility
What Makes Kyozir Multilayer Zirconia Different?
Unlike traditional single-layer zirconia discs, Kyozir multilayer zirconia is designed with a biomimetic gradient structure, simulating natural enamel-to-dentin transition.
This improves:
- Anterior esthetics
- Cervical strength stability
- Incisal translucency balance
Physical Characteristics
| Property | Value |
|---|---|
| Density before sintering | 3.15±0.05 g/cm³ |
| Density after sintering | 6.07±0.02 g/cm³ |
| CTE (25-500℃) | (10.4±0.5)×10⁻⁶ K⁻¹ |
| Accelerated aging surface monoclinic phase content | <15% |
| Chemical solubility after sintering | <100 μg/cm |
| Radioactivity | <0.1 Bq/g |
| Sintering temperature | 1530℃ |
Clinical Applications
Full Contour Anterior Crown
Posterior Bridge (3 units)
Full Contour Bridge (4 units)
Full Contour Bridge (>4 units)
Anterior Coping
Reduced Posterior Bridge (3 units)
Posterior Coping
Anterior Coping Bridge (3 units)
Why Choose Kyozir?
Direct Factory Supply - Kyozir
- 15+ years of dental zirconia manufacturing experience
- Advanced CAD/CAM material R&D system
- Strict ISO / CE / FDA certified production
- Stable raw material supply
- Exported to 60+ countries worldwide
Quality Assurance System
- Raw material inspection before production
- Density & purity testing
- Flexural strength testing
- Translucency consistency check
- Sintering shrinkage verification
- Final batch QC before shipment
Our Technical Advantage
- Uniform particle distribution technology
- Controlled sintering shrinkage system
- Layer gradient stability control
- High consistency batch production system
You May Also Like